| Alloy | Grade | chemical composition % | |||||
| Mg | Al | Zn | Mn | Ce | Zr | ||
| Mg | Mg99.95 | ≥99.95 | ≤0.01 | - | ≤0.004 | - | - |
| Mg99.50 | ≥99.5 | - | - | - | - | - | |
| Mg99.00 | ≥99.0 | - | - | - | - | - | |
| MgAlZn | Az31B | Bal. | 2.5-3.5 | 0.60-1.4 | 0.20-1.0 | - | - |
| AZ31S | Bal. | 2.4-3.6 | 0.50-1.5 | 0.15-0.40 | - | - | |
| AZ31T | Bal. | 2.4-3.6 | 0.50-1.5 | 0.05-0.04 | - | - | |
| AZ40M | Bal. | 3.0-4.0 | 0.20-0.80 | 0.15-0.50 | - | - | |
| Az41M | Bal. | 3.7-4.7 | 0.80-1.4 | 0.30-0.60 | - | - | |
| AZ61A | Bal. | 5.8-7.2 | 0.40-1.5 | 0.15-0.50 | - | - | |
| AZ80A | Bal. | 7.8-9.2 | 0.20-0.80 | 0.12-0.50 | - | - | |
| Az80M | Bal. | 7.8-9.2 | 0.20-0.80 | 0.15-0.50 | - | - | |
| AZ80S | Bal. | 7.8-9.2 | 0.20-0.80 | 0.12-0.40 | Â | - | |
| Az91D | Bal. | 8.5-9.5 | 0.45-0.90 | 0.17-0.40 | - | - | |
| MgMn | M1C | Bal. | ≤0.01 | - | 0.50-1.3 | - | - |
| M2M | Bal. | ≤0.20 | ≤0.30 | 1.3-2.5 | - | - | |
| M2S | Bal. | - | - | 1.2-2.0 | - | - | |
| MgZnZr | Zk61M | Bal. | ≤0.05 | 5.0-6.0 | ≤0.10 | - | 0.30-0.90 |
| Zk61S | Bal. | - | 4.8-6.2 | - | - | 0.45-0.80 | |
| MgMnRE | Me20M | Bal. | ≤0.020 | ≤0.30 | 1.3-2.2 | - | - |
| Grade | Condition | Diameter/mm | Tensile Strength Rm/MPa | Rp0.2/Mpa | Elongation A/% |
| AZ31B | H112 | ≤130 | 220 | 140 | 7.0 |
| AZ40M | H112 | ≤100 | 245 | - | 6.0 |
| 100-130 | 245 | - | 5.0 | ||
| Az41M | H112 | ≤130 | 250 | - | 5.0 |
| AZ61A | H112 | ≤130 | 260 | 160 | 6.0 |
| AZ61M | H112 | ≤130 | 265 | - | 8.0 |
| Â Az80A |
H112 | ≤60 | 295 | 195 | 6.0 |
| 60-130 | 290 | 180 | 4.0 | ||
| T5 | ≤60 | 325 | 205 | 4.0 | |
| 60-130 | 310 | 205 | 2.0 | ||
| Â ME20M |
 H112 |
≤50 | 215 | - | 4.0 |
| 50-100 | 205 | - | 3.0 | ||
| 100-130 | 195 | - | 2.0 | ||
| ZK61M | T5 | ≤100 | 315 | 245 | 6.0 |
| 100-130 | 305 | 235 | 6.0 | ||
| Zk61S | T5 | ≤130 | 310 | 230 | 5.0 |
1.Transportation:
 Seat frame, armrest, small table panel, pedal, in-built profiles, driving frame, sleeper frame work, dashboard frame work etc.
2.Electronics:
Magnesium alloys have excellent thin wall casting performance. They wall thickness of magnesium alloy die castings can reach 0.6-1.0mm, and the die castings can remain certain strength, stiffness and impact resistance. These performances are very consistent with development demand of lightweight, thin short and small for laptop. Mobile phone, digital camera, that makes the application of magnesium alloy grow sustainably.
3.Aerospace industry:
Engine shell, parts. Skin and cabin, frame, holder, wingtip, aileron, fuel tank, gearbox, airscrew, seat, undercarriage, all kinds of shell, siding, clapboard etc.
4.Military industry:
Panzer tank vehicle, torpedo, guided missile, aircraft / spacecraft, military electronic equipment, military statellite.
5.Medical industry:
Medical device and implant material.
Â
Â
Dimensions: Standard diameters: 1.2mm, 1.6mm, 2.0mm, 2.4mm, 3.0mm ,4.0mm
High quality magnesium alloy welding wire
Packaging: Every reel is packed in vacuum foil package, the reels are packed in wooden case
extruded
pure magnesium wire
Diametre: 1.2mm to 4.0mm or bigger
| AZ31 | GB/T 5153 | |||||||
| Elements | Â Al | Â Zn | Â Mn | Â Si | Â Fe | Â Cu | Â Ni | Â Others,total |
| Â Min% | Â 2.40 | Â 0.50 | Â 0.15 | Â | Â | Â | Â | Â |
| Â Max% | Â 3.60 | Â 1.50 | Â 0.4 | Â 0.10 | Â 0.005 | Â 0.05 | Â 0.005 | Â 0.3 |
| AZ61 | GB/T 5153 | |||||||
| Â Elements | Â Al | Â Zn | Â Mn | Â Si | Â Fe | Â Cu | Â Ni | Â Others,total |
| Â Min% | Â 5.50 | Â 0.5 | Â 0.15 | Â | Â | Â | Â | Â |
| Â Max% | Â 6.50 | Â 1.50 | Â 0.40 | Â 0.10 | Â 0.005 | Â 0.05 | Â 0.005 | Â 0.3 |
| AZ91 | GB/T 5153 | ||||||||
| Elements |  Al |  Zn |  Mn |  Si |  Fe |  Cu | Ni |  Be |  Others,total |
| Min% | Â 8.5 | Â 0.45 | Â 0.17 | Â | Â | Â | Â | Â 0.0005 | Â |
| Max% | Â 9.5 | Â 0.90 | Â 0.40 | Â 0.08 | Â 0.004 | Â 0.025 | Â 0.001 | Â 0.003 | Â 0.3 |
| AZ92 | AWS A5.19-1992 | ||||||||
| Elements |  Al |  Zn |  Mn |  Si |  Fe |  Cu | Ni | Be | Commercial Plywood is the basic wooden product for furniture, is one of the biggest wooden products, is used for plane, boat, train, bus, construction and package etc. It is the one of the main way to save wood resource and improve the usage of wood.Usually poplar, pine, combi, hardwood as the core, the bace&back are the Veneer surface, such as Okoume, Bintangor, Pine, Birch, Poplar, Pencil cedar, Maple, Cherry, White Oak, Sapele, Beech, Red Oak, Ash etc. LULI Group Corp. Ltd, well known as the leading manufacturer for wooden, steel and paper products, located in Shouguang, Weifang, Shandong, China. Since the foundation in 1985, it focus on the production of commercial Plywood , venner, MDF , Particle board, Door skin , Blockboard, Finger Joint Board, OSB , paper, Steel etc. And we have High Quality commercial Plywood. Advantages: 1.High bending strength 2.Strong nail holding 3.Moisture-proof and easy work 4.Tight construction and high strength 5.No ratten or decay 6.Low formaldehyde emission 7.The productions are suitable for the construction of viaduct and tall frame building 8.If put in boiling water for 48 hours,it still glue sticking and still formed 9.If used abide by illustration strictly,it can be reuse more than 50 times 10.Solve the problem of leaking and rough surface during construction process.Particular suiltable for watering concreat. Commercial plywood Details: size:1220*2440mm 1220*3000mm 915*1830mm 1250*2500mm, according requirement thickness:2mm-60mm core:poplar/combine/hardwood glue:MR/E2/E1/E0/melamine/WBP kinds:okoume,bintangor,pine,birch,poplar,cedar,ect. certification:CARB,FSC,CE,JAS,ISO9001,ISO14001